T 30 G is a polypropylene homopolymerfor injection moulding applications. T 30 G combines high stiffness and fairiy good impact strength with good processability. The grade is suitable for a wide range of applications such as housewares, caps, closures, small containers, toys, parts for small appliances and components for the automotive industry ..
| Properties | Unit | Typical value | Test Method |
| Physical properties | |||
| Melt flow rate (230'C, 2.16 kg) | Dg/min | 3.2 | ISO 1133 |
| Density | g/cm3 | 0.9 | ISO 1183 |
| Mechanical properties | |||
| Flexural modulus | N/mm2 | 1450 | ISO 178 |
| Tensile strength yield | N/mm2 | 34 | ISO R527 |
| Elongation at yield | % | 13 | ISO R 527 |
| lzod impact strenghh (notched) at 23 °C | kJ/m2 | 5 | ISO 180 |
| Hardness Shore D | points | 71 | ISO 868) |
| Thermal properties | |||
| Vicat softening point (9.8 N) | oC | 155 | ISO 306/A |
| H.D.T. (0.46 Mpa) | oC | 110 | ISO 75/B |
| Accelerated oven ageing in air (forced circulation) at 150 °C | hour | 360 | IS04577 |
It is suitable for food contact.
Values shown are averages and are not to be considered as p roduct specification
These values may shift slightly as additional data are accumlsted.
ISO test methods are the lates under the societys current procedures. All specimens
are prepared by injection moulding .