Homo Polymer

Polypropylene Homopolymer for Production of Fine Denier Staple Fibres for Nonwoven Thermobonded Fabrics. Product Description: • Fabrics made with Parslen ZH554N are characterized by softness, textile-l ike appearance and high tear resistance. • In comparison with standard Polypropylene types for thermobnding applications, Parslen ZH554N offers some distinct advantages. • The processability with the tong-spinning technology is outstanding, resulting in hig h and uniform fibre quality and less down-time. • Parslen ZH554N gives a broad thermal bonding window, which facilitates start-up and adjustments of the plant. • Parslen ZH554N shows a 20 to 30 % increase in thermal bonding ability. This makes it possible to produce fabrics with a higher tear strength or with tower weight per m2 for the same strength. Application: • The fabrics are particularly suited for the production of fabrics for feminine care products, diapers, incontinence pads, medical disposables, wipes and other applications include filters and fabrics for the automotive, clothing and furniture industry.

General Properties

Category : Homo Polymer
Grade Name : 554N(ZH554N)
Manufacturer : NAVID ZAR CHIMI
MFR : 7.1-12
Density : 0.954
Applications :
Heavy duty jumbo bags,Furniture,Caps,Closures,Toys
Typical Properties Method Unit Value(a) Tolerance
Melt flow rate(230 ° C, 2.16 Kg) ASTM D 1238 gr/10 min 12 ±2
Vicat soften ing point ( 9.8 N) ASTM D 1525 •c 155 ±4
H.0.T. (0.46 MPa) ASTM 0648 •c 117 ±10
Flexural modulus ASTM O 790 MPa 1550 ±150
Tensile strength at yield ASTM 0638 MPa 35 ±5
Elongation at yield ASTM 0638 % 13 -2
lzod impact strength( notched ) at 23° C ASTM 0256 J/m 35 ±4
Rockwell hardness (R -B Scale] ASTM D0785 R-B 71 ±10

Values shown are averages and are not to be considered as exact product

All specimens are prepared by injection molding.

 It is suitable for food contact