POLYMER TYPE: POLYPROPYLENE HOMOPOLYMER PACKING: PP bags of 25 kgs, 50 bags on a pallet shrinked by PE APPLICATION : : High stiffness thermoformed parts, special extrusion applications PRODUCT FEATURES: Homopolymer with high stiffness PROCESSING METHOD: Extrusion
| Property | Test Method | Unit | Value |
| MFR ( 230 ̊ C/ 2.16 Kg ) | ASTM D1238/L | gr/10min | 11 |
| Tensile Modulus of Elasticity (1mm/min) | ASTM D638 | MPa | 2000 |
| Tensile Strength at Yield (50 mm/min) | ASTM D638 | MPa | 40 |
| Elongation at Yield(50 mm/min) | ASTM D638 | % | 7 |
| Notched Charpy Impact at 23 ̊ | ISO 179/ 1eA | KJ/m2 | 3 |
| Notched Charpy Impact at -30 ̊ | ISO 179/ 1eA | KJ/m2 | 1.5 |
| Vicat Softening Point, 10N | ASTM D1525 | ̊C | 158 |
| Ball indentation hardness | ISO 2039-1 | MPa | 93 |
| HDT ( 0.46 N/mm2 ) | ASTM D648 | ̊C | 110 |
| Melting Point , DSC | ASTM D3417 | ̊C | 165 |
| Density | ASTM D792 | gr/cm3 | 0.91 |