Classification: General grade. Characteristic: high flow Application: ABS Compounding, Electrical &electronic parts, Flow meter case&etc .
| Property | Test method (ASTM) | Test condition | Unit | Typical value | SAN-3Specification | |
| Izod impact | D-256 | 6.4 mm , notched | Kj/m² | 1.5 | Min1.5 | |
| Melt flow index | D-1238 | 220ºc , 10 kg | gr/10 min | 12 | 10-15 | |
| Rock well hardness | D-785 | ........ | R-scale | 86 | Min85 | |
| HDT | D-648 | 1.82 m pa | ºc | 93 | Min88 | |
| Vicat softening Temp | D-1525 | 5kg/50°c | ºc | 108 | Min 97 | |
| Tensile strength | D-638 | 23ºc , 50 mm/min | Kg/cm² | 800 | Min730 | |
| Tensile elongation | D-638 | 23ºc , 50 mm/min | % | 1050 | Min 900 | |
| Flexural strength | D-790 | 23ºc , 2.8 mm/min | Kg/cm² | 32500 | Min 32000 | |
| Flexural Modulus | D-790 | 23ºc , 2.8 mm/min | Kg/cm² | 0.3 | 0.3 | |
| Specific Gravity | D-792 | 23ºc | .. | 1.04 | 1.04 | |
| Molding Shrinkage | D-955 | ... | % | 0.2~0.6 | 0.2~0.6 | |
| Flammability | Ul94 | 1/8inch(3.2mm) | ... | HB | HB | |
| Rear Temp(°c) | Center Temp (°c) | Center Temp (°c) | Front Temp (°c) | Nozzle Temp(°c) | Melt Temp (°c) | |
| 190-200 | 200-210 | 210-220 | 210-220 | 215-225 | 230 | |
| Mold Temp (°c) | Filling Speed | - | - | - | - | |
| 60-80 | Slow-Med | - | - | - | - | 110 |
TYPICAL ABS PROCESSING CONDITIONS
DRYING: it is recommended that GBPC SAN Resins be dried at (80-85°c)for 3 hours.
The following molding conditions are recommended starting point for GBPC ABS Resin. A
moisture level of ≤0.1% should be reached before injection molding the resin. Some
modifications may be required depending on the specific molding equipment and part
configuration.