1922(L1922T)

1922(L1922T)

LDPE


General Properties

Category : LDPE
Grade Name : 1922(L1922T)
Manufacturer : LALEH
MFR : 2.2(2.16k/g)
Density : 919(kg/m3)
Applications :
The grade especially developed for applications requiring a good balance between flow properties and mechanical properties,e.g.toys,houseware,snap-on lids.
Properties Unit Typical value Test Method
Polymer Properties
Density kg/m3 919
Melt Flow Rate (MFR)
at 190 ̊C and 2.16 kg dg/min 22
at 190 ̊C and 5 kg dg/min 75
Melt Volume Rate (MVR)
at 190 ̊C and 2.16 kg dg/10 min 29
at 190 ̊C and 2.16 kg dg/10 min 98
Mechanical properties
Tensile test
Stress at yield MPa 8
Stress at break MPa 7
Strain at break % 400
Tensile modulus MPa 175
Creep modulus
after 1 hour MPa 80
after 1000 hour MPa 45
Notched Izod
at + 23 ̊C KJ/m2 42
at - 30 ̊ C KJ/m2 5
Tensile impact test
Notched tensile impact strength KJ/m2 86
Elongation at break % 84
Maximum tension MPa 16
Hardness Shore D - 45
Ball indentation test
Applied load N 49
Ball indentation hardness MPa 16
ESCR H 3
Termal properties
Heat deflection
temperature
at 0.45 MPa (HDT/B) o C 39
Vicat softening
temperature
at 10 n (VST/A) o C 82
DSC test
Melting point 12) o C 105
Enthalpy change J/g 104

Application
The material is intended for very thin film requiring very good optical properties and is thus
mainly applied in general packaging film such as textile packaging.
General information
LPC produces low density polyethylene by the tubular reactor process. As a result the product
range covers a wide variety of densities and melt flow rates. The LDPE grade slate has a wide
variety of slip and anti block additives levels and includes a large numbers of grades with
excellent optical properties. LPC tubular production technology guarantees a very low gel level
and outstanding draw down ability, low odor and taste levels, which is of advantage for thin
film processing and e.g. food packaging.
Quality
LPC is fully certified in accordance with the internationally accepted quality standard ISO
9001-2000.It is LPC policy to supplymaterials that meet customers specifications and needs
and to keep up its reputation as a pre eminent, reliable supplier of e.g. polyethylene.

Environment
The environmental aspects of any packaging material do not only imply waste issues but have
to be considered in relation with the use of natural resources, the preservations of foodstuffs,
etc.LPC considers polyethylene to be an environmentally efficient packaging material. Its low
specific energy consumption and insignificant emissions to air and water designate
polyethylene as the ecological alternative in comparison with the traditional packaging
materials.
Recycling
Recycling of packaging materials is supported by LPC whenever ecological and social
benefits are achieved and where a social infrastructure for selective collecting and sorting of
packaging is fostered.Whenever ‘thermal’ recycling of packagings (i.e.incineration with
energy recovery)is carried out,polyethylene –with its fairly simple molecular structure and
low amount of additives-is considered to be a trouble-free fuelpackaging
Food approvals
The converter/food packager is responsible for compliance of the performance of the final
article under foreseeable conditions of use. More specific information on the regulatory aspects
of the LPC polyethylene is available in the relevant Food Approval Declarations which can be
obtained from LPC Sales Office..
Safety
Under normal conditions polyethylenes do not present a toxic hazard through skin contact or
inhalation. During processing contact with molten polymer and inhalation of volatilized fumes
should be avoided. It is recommended to install exhaust hoods over processing machines and
to keep working area well ventilated. More specific information on the safety aspects of the
LPC polyethylenes are provided in the relevant Material Safety Data Sheets, available from
LPC Sales Office.

Storage
As polyethylenes ,like most polymers, are combustible ,the usual precautions concerning
ignition sources should be taken in warehouses and storage rooms. where large quantities are
kept in store, it is necessary to observe the normal rules for orderly stock control and to keep
out dust and moisture. Polyethylenes should be stored in such a way as to prevent exposure to
direct sunlight, as this may lead to quality deterioration.
Disclaimer
The information contained herein may include typical properties of our products or their typical
performances when used in certain typical applications. Actual properties of our products, in
particular when used in conjunction with any third party material(s) or for any non-typical
applications, may differ from typical properties. It is the customer’s responsibility to inspect
and test our product(s) in order to satisfy itself as to the suitability of the product(s) for its and
its customers particular purposes. The customer is responsible for the appropriate ,safe and
legal use, processing and handling of all product(s) purchased from us. Nothing herein is
intended to be nor shall it constitute a warranty whatsoever, in particular, warranty of
merchantability or fitness for a particular purpose


SHARE:

OUR PRODUCTS