POLYMER TYPE: POLYPROPYLENE HOMOPOLYMER PACKING : PP bags of 25 kgs, 50 bags on a pallet shrinked by PE APPLICATION : Bulk continuous filaments(BCF) and continuous filaments(CF) with higher resilience PRODUCT FEATURES : Homopolymer with resistance to gasfading PROCESSING METHOD : Extrusion
| Property | Test Method | Unit | Value |
| MFR ( 230 ̊ C/ 2.16 Kg ) | ASTM D1238/L | gr/10min | 15.5 |
| Tensile Modulus of Elasticity (1mm/min) | ASTM D638 | MPa | 1500 |
| Tensile Strength at Yield (50 mm/min) | ASTM D638 | MPa | 35 |
| Elongation at Yield(50 mm/min) | ASTM D638 | % | 10 |
| Notched Charpy Impact at 23 ̊ | ISO 179/ 1eA | KJ/m2 | 2.5 |
| Notched Charpy Impact at - 30 ̊ | ISO 179/ 1eA | KJ/m2 | 1.5 |
| Vicat Softening Point, 10N | ASTM D1525 | ̊C | 154 |
| Ball indentation hardness | ISO 2039-1 | MPa | 70 |
| HDT ( 0.46 N/mm2 ) | ASTM D648 | ̊C | 85 |
| Melting Point , DSC | ASTM D3417 | ̊C | 163 |