Classification: General grade. Characteristic: high flow Application: ABS Compounding, disposable lighter, pounding, Electrical &electronic parts,&etc
Property | Test method (ASTM) | Test condition | Unit | Typical value | SAN-5 Specification | |
Izod impact | D-256 | 6.4 mm , notched | Kj/m² | 2 | Min2.5 | |
Melt flow index | D-1238 | 220ºc , 10 kg | gr/10 min | 5.5 | 3-7 | |
Rock well hardness | D-785 | ........ | R-scale | 92 | Min90 | |
HDT | D-648 | 1.82 m pa | ºc | 94 | Min90 | |
Vicat softening Temp | D-1525 | 5kg/50°c | ºc | 110 | Min 99 | |
Tensile strength | D-638 | 23ºc , 50 mm/min | Kg/cm² | 900 | Min800 | |
Tensile elongation | D-638 | 23ºc , 50 mm/min | % | 1150 | Min 1250 | |
Flexural strength | D-790 | 23ºc , 2.8 mm/min | Kg/cm² | 33500 | Min 33000 | |
Flexural Modulus | D-790 | 23ºc , 2.8 mm/min | Kg/cm² | 0.3 | 0.3 | |
Specific Gravity | D-792 | 23ºc | .. | 1.04 | 1.04 | |
Molding Shrinkage | D-955 | ... | % | 0.2~0.6 | 0.2~0.6 | |
Flammability | Ul94 | 1/8inch(3.2mm) | ... | HB | HB | |
Rear Temp(°c) | Center Temp (°c) | Center Temp (°c) | Front Temp (°c) | Nozzle Temp(°c) | Melt Temp (°c) | |
190-200 | 200-210 | 210-220 | 210-220 | 215-225 | 230 | |
Mold Temp (°c) | Filling Speed | - | - | - | - | |
60-80 | Slow-Med | - | - | - | - | 110 |
TYPICAL ABS PROCESSING CONDITIONS
DRYING: it is recommended that GBPC SAN Resins be dried at (80-85°c)for 3 hours.
The following molding conditions are recommended starting point for GBPC ABS Resin. A
moisture level of ≤0.1% should be reached before injection molding the resin. Some
modifications may be required depending on the specific molding equipment and part
configuration