SAN-1

SAN-1

ABS

Classification: General grade. Characteristic: high flow Application: ABS Compounding ,ABS/PC Compounding,Cups,cosmetic container, Blower fan, pencil case, juicer, stereo dust cover&etc


General Properties

Category : ABS
Grade Name : SAN-1
Manufacturer : GHAED BASIR
MFR : 20-30
Density : 0.954
Applications :
ABS Compounding ,ABS/PC Compounding,Cups,cosmetic container, Blower fan, pencil case, juicer, stereo dust cover&etc
Property Test method (ASTM) Test condition Unit Typical value SAN-1 Specification
Izod impact D-256 6.4 mm , notched Kj/m² 1.5 Min2
Melt flow index D-1238 220ºc , 10 kg gr/10 min 30 28-32
Rock well hardness D-785 ........ R-scale 83 Min81
HDT D-648 1.82 m pa ºc 92 Min88
Vicat softening Temp D-1525 5kg/50°c ºc 105 Min 98
Tensile strength D-638 23ºc , 50 mm/min Kg/cm² 680 Min 620
Tensile elongation D-638 23ºc , 50 mm/min % 750 Min 670
Flexural strength D-790 23ºc , 2.8 mm/min Kg/cm² 31500 Min 31000
Flexural Modulus D-790 23ºc , 2.8 mm/min Kg/cm² 0.3 0.3
Specific Gravity D-792 23ºc .. 1.04 1.04
Molding Shrinkage D-955 ... % 0.2~0.6 0.2~0.6
Flammability Ul94 1/8inch(3.2mm) ... HB HB
Rear Temp(°c) Center Temp (°c) Center Temp (°c) Front Temp (°c) Nozzle Temp(°c) Melt Temp (°c)
190-200 200-210 210-220 210-220 215-225 230
Mold Temp (°c) Filling Speed - - - -
60-80 Slow-Med - - - - 110

TYPICAL ABS PROCESSING CONDITIONS
DRYING: it is recommended that GBPC SAN Resins be dried at (80-85°c)for 3 hours.

The following molding conditions are recommended starting point for GBPC ABS Resin. A
moisture level of ≤0.1% should be reached before injection molding the resin. Some
modifications may be required depending on the specific molding equipment and part
configuration.