Classification: General grade ABS>Flame retardant Characteristic: medium Impact Strength > Flame retardant Application: Electrical and Electronic parts,TV,VTR,Printer,facsmilie,computer,monitor&requiring flame retardant property.
| Property | Test method (ASTM) | Test condition | Unit | Typical value | Final Product specification |
| Izod impact | D-256 | 6.4 mm , notched | Kj/m² | 21 | Min18 |
| Melt flow index | D-1238 | 220ºc , 10 kg | gr/10 min | 50 | 40-50 |
| Rock well hardness | D-785 | ........ | R-scale | 112 | 95-115 |
| HDT | D-648 | 1.82 m pa | ºc | 84 | Min82 |
| Vicat softening Temp | D-1525 | 5kg/50°c | ºc | 94 | Min 93 |
| Tensile strength | D-638 | 23ºc , 50 mm/min | Kg/cm² | 440 | Min 420 |
| Tensile elongation | D-638 | 23ºc , 50 mm/min | % | 30 | Min 18 |
| Flexural strength | D-790 | 23ºc , 2.8 mm/min | Kg/cm² | 650 | Min 630 |
| Flexural Modulus | D-790 | 23ºc , 2.8 mm/min | Kg/cm² | 20000 | Min18000 |
| Specific Gravity | D-792 | 23ºc | .. | 1.16 | 1.16 |
| Molding Shrinkage | D-955 | ... | % | 0.4-0.7 | 0.4-0.7 |
| Flammability | Ul94 | 1/8inch(3.2mm) | ... | HB | HB |
| Rear Temp(°c) | Center Temp (°c) | Center Temp (°c) | Front Temp (°c) | Nozzle Temp(°c) | Melt Temp (°c) |
| 190-200 | 200-210 | 210-220 | 210-220 | 215-225 | 230 |
| Mold Temp (°c) | Filling Speed | - | - | - | - |
| 60-80 | Slow-Med | - | - | - | - |
TYPICAL ABS PROCESSING CONDITIONS
DRYING: it is recommended that GBPC ABS Resins be dried at (80-85°c)for 3 hours.
The following molding conditions are recommended starting point for GBPC ABS Resin. A
moisture level of ≤0.1% should be reached before injection molding the resin.
Some modifications may be required depending on the specific molding equipment and part
configuration