Classification: General purpose Characteristic: Medium Impact, High rigidity Application: Electronic and Electrical parts, vacuum cleaner, washing machine cover and Refrigeratordoor cap & etc
Property | Test method (ASTM) | Test condition | Unit | Typical value | ABS-80 Specification |
Izod impact | D-256 | 6.4 mm , notched | Kj/m² | 20 | Min16 |
Melt flow index | D-1238 | 220ºc , 10 kg | gr/10 min | 52 | 45-55 |
Rock well hardness | D-785 | ........ | R-scale | 110 | 100-120 |
HDT | D-648 | 1.82 m pa | ºc | 85 | Min82 |
Vicat softening Temp | D-1525 | 5kg/50°c | ºc | 95 | Min 93 |
Tensile strength | D-638 | 23ºc , 50 mm/min | Kg/cm² | 470 | Min 450 |
Tensile elongation | D-638 | 23ºc , 50 mm/min | % | 19 | Min 14 |
Flexural strength | D-790 | 23ºc , 2.8 mm/min | Kg/cm² | 670 | Min 650 |
Flexural Modulus | D-790 | 23ºc , 2.8 mm/min | Kg/cm² | 22000 | Min20000 |
Specific Gravity | D-792 | 23ºc | .. | 1.04 | 1.04 |
Molding Shrinkage | D-955 | ... | % | 0.4-0.7 | 0.4-0.7 |
Flammability | Ul94 | 1/8inch(3.2mm) | ... | HB | HB |
Rear Temp(°c) | Center Temp (°c) | Center Temp (°c) | Front Temp (°c) | Nozzle Temp(°c) | Melt Temp (°c) |
190-200 | 200-210 | 210-220 | 210-220 | 215-225 | 230 |
Mold Temp (°c) | Filling Speed | - | - | - | - |
60-80 | Slow-Med | - | - | - | - |
TYPICAL ABS PROCESSING CONDITIONS
DRYING: it is recommended that GBPC ABS Resins be dried at (80-85°c)for 3 hours.
The following molding conditions are recommended starting point for GBPC ABS Resin. A
moisture level of ≤0.1% should be reached before injection molding the resin.
Some modifications may be required depending on the specific molding equipment and part
configuration