Classification: General purpose Characteristic: Medium Impact, High rigidity Application: Electronic and Electrical parts, vacuum cleaner, washing machine cover and Refrigeratordoor cap & etc
| Property | Test method (ASTM) | Test condition | Unit | Typical value | ABS-70Specificati on |
| Izod impact | D-256 | 6.4 mm , notched | Kj/m² | 26 | Min23 |
| Melt flow index | D-1238 | 220ºc , 10 kg | gr/10 min | 14 | 8-16 |
| Rock well hardness | D-785 | ........ | R-scale | 113 | 100-120 |
| HDT | D-648 | 1.82 m pa | ºc | 90 | Min85 |
| Vicat softening Temp | D-1525 | 5kg/50°c | ºc | 100 | Min96 |
| Tensile strength | D-638 | 23ºc , 50 mm/min | Kg/cm² | 470 | Min440 |
| Tensile elongation | D-638 | 23ºc , 50 mm/min | % | 25 | Min18 |
| Flexural strength | D-790 | 23ºc , 2.8 mm/min | Kg/cm² | 670 | Min650 |
| Flexural Modulus | D-790 | 23ºc , 2.8 mm/min | Kg/cm² | 23000 | Min20000 |
| Specific Gravity | D-792 | 23ºc | .. | 1.04 | 1.04 |
| Molding Shrinkage | D-955 | ... | % | 0.4-0.7 | 0.4-0.7 |
| Flammability | Ul94 | 1/8inch(3.2mm) | ... | HB | HB |
| 190-200 | 200-210 | 210-220 | 210-220 | 220-230 | 190-200 |
| Zone 1(°c) | Zone 2(°c) | Zone 3(°c) | Zone 4(°c) | Zone 5(°c) | Zone 6(°c) |
| 190-200 | 190-200 | 200-210 | 200-210 | 210-220 | 210-220 |
| Adapter(°c) | Die zone(°c) | Screen Pack Mesh (2layer) | - | - | - |
| 210-220 | 225-235 | #60-80 | - | - | - |
| Rear Temp(°c) | Center Temp (°c) | Center Temp (°c) | Front Temp (°c) | Nozzle Temp (°c) | Melt Temp (°c) |
| 190-200 | 200- 210 | 210- 220 | 245- 225 | 225- 235 | 240 |
| Mold Temp (°c) | Filling Speed | - | - | - | - |
| 60-80 | Slow- Med | - | - | - | - |
TYPICAL ABS PROCESSING CONDITIONS
DRYING: it is recommended that GBPC ABS Resins be dried at (80-85°c)for 3 hours.
The following molding conditions are recommended starting point for GBPC ABS Resin. A
moisture level of ≤0.1% should be reached before injection molding the resin.
Some modifications may be required depending on the specific molding equipment and part
configuration.
INJECTION MOLDIN CONDITION
Some modifications may be required depending on the specific molding
equipment and part configuration