Classification: General purpose Characteristic: High Impact Resistance Applicatins: Automobile parts(radiator grill &etc.),Helmets,Toys,Suitcase,shoe heels,skis,Golf clubheads, Sports equipment,suitcases,&etc.
| Property | Test method (ASTM) | Test condition | Unit | Typical value | ABS-40Specification |
| Izod impact | D-256 | 6.4 mm , notched | Kj/m² | 32 | Min26 |
| Melt flow index | D-1238 | 220ºc , 10 kg | gr/10 min | 25 | 18-28 |
| Rock well hardness | D-785 | ........ | R-scale | 98 | 90-110 |
| HDT | D-648 | 1.82 m pa | ºc | 82 | Min 82 |
| Vicat softening Temp | D-1525 | 5kg/50°c | ºc | 92 | Min 93 |
| Tensile strength | D-638 | 23ºc , 50 mm/min | Kg/cm² | 400 | Min 390 |
| Tensile elongation | D-638 | 23ºc , 50 mm/min | % | 30 | Min 25 |
| Flexural strength | D-790 | 23ºc , 2.8 mm/min | Kg/cm² | 580 | Min 530 |
| Flexural Modulus | D-790 | 23ºc , 2.8 mm/min | Kg/cm² | 18000 | Min 15000 |
| Specific Gravity | D-792 | 23ºc | .. | 1.04 | 1.04 |
| Molding Shrinkage | D-955 | ... | % | 0.4-0.7 | 0.4-0.7 |
| Flammability | Ul94 | 1/8inch(3.2mm) | ... | HB | HB |
| Rear Temp(°c) | Center Temp (°c) | Center Temp (°c) | Front Temp (°c) | Nozzle Temp(°c) | Melt Temp (°c) |
| 190-200 | 200-210 | 210-220 | 210-220 | 215-225 | 230 |
| Mold Temp (°c) | Filling Speed | - | - | - | - |
| 60-80 | Slow-Med | - | - | - | - |
TYPICAL ABS PROCESSING CONDITIONS
DRYING: it is recommended that GBPC ABS Resins be dried at (80-85°c)for 3 hours.
The following molding conditions are recommended starting point for GBPC ABS Resin. A
moisture level of ≤0.1% should be reached before injection molding the resin.
Some modifications may be required depending on the specific molding equipment and part
configuration.