2340(HR2340)

2340(HR2340)

ABS

HR2340 is one of the styrenic terpolymer(ABS) grade with improved toughness and heat resistance versus HIPS grades. HR2320 exhibits low shrinkage and good dimensional stability. HR2320 is widely used in general injection molding applications.Use this information as a guide to aid you in selecting the proper resin for your application. Application: furniture,automotive parts ,general injection molding,appliances casing and home appliances with heatresistance characteristics. Drying: Drying prior to processing is recommended in a desiccant dehumidifying hopper dryer. An inlet air dew point of - 20°F (-29°C) or below isrecommended to achieve a moisture content 0.1%. Typical drying conditions are 2 hours at 180° - 190°F (82°-88°C). Drying for 4 hoursat 160° - 170°F (71°-77°C) is also adequate


General Properties

Category : ABS
Grade Name : 2340(HR2340)
Manufacturer : TABRIZ
MFR : 1.2(5k/g)
Density : 0.954
Applications:
furniture,automotive parts ,general injection molding,appliances casing and home appliances with heat resistance characteristics.
Properties Unit Typical value Test Method
MELT FLOW INDEX(200°C-5KG) g/10min 1 ASTM D-1238
IZOD IMPACT STRENGTH KJ/M2 40 ASTM D-256
VICAT SOFTENING POINT ( 50 °C/hr 1kg) oC 112 ASTM D-1525
BULK DENSITY KG/M3 600 -
TENSILE STRESS AT YEILD KGF/CM2 480 ASTM D-638
ROCKWELL HARDNESS(AT 23°C) R.SCALE 110 ASTM D-785

*All above mentioned data are typical values and not to be construed as real specifications.Users should confirm results by
their own tests.For more

information about guaranteed items, please refer to S.S.S.(Standard Sales Specifications)