POLYMER TYPE: POLYPROPYLENE HOMOPOLYMER PACKING : PP bags of 25 kgs, 50 bags on a pallet shrinked by PE APPLICATION : Preferred grade for BCF/CF, carpet yarns, POY/DTY, extrusion laminating PRODUCT FEATURES : Homopolymer with antigasfading stabilization and inherent UV stability PROCESSING METHOD : Extrusion
Property | Test Method | Unit | Value |
MFR ( 230 ̊ C/ 2.16 Kg ) | ASTM D1238/L | gr/10min | 24 |
Tensile Modulus of Elasticity (1mm/min) | ASTM D638 | MPa | 1500 |
Tensile Strength at Yield (50 mm/min) | ASTM D638 | MPa | 35 |
Elongation at Yield(50 mm/min) | ASTM D638 | % | 8 |
Notched Charpy Impact at 23 ̊ | ISO 179/ 1eA | KJ/m2 | 2.5 |
Notched Charpy Impact at - 30 ̊ | ISO 179/ 1eA | KJ/m2 | 1.5 |
Vicat Softening Point, 10N | ASTM D1525 | ̊C | 154 |
Ball indentation hardness | ISO 2039-1 | MPa | 78 |
HDT ( 0.46 N/mm2 ) | ASTM D648 | ̊C | 85 |
Melting Point , DSC | ASTM D3417 | ̊C | 163 |
Density | ASTM D792 | gr/cm3 | 0.91 |